Mold cavity has a smooth-polished surface and your ABS molding part is too dull?

Have you ever met the case when the cavity steel has been polished as high as possible but the ABS molded part is still not at the gloss needed? The problem may be related to mould, material, processing, or combinations thereof. Look at below information to find the root cause.

 

Plastic injection Mold

 

  1. Surface of cavity steel is not clean

Oil or water stain on the surface of cavity steel, and too much release agent applied during the process of abs injection molding, all this create a dull appreance. In this case, clean the mould and control the use of mold release agents.

 

  1. Mold or Part design

 

When the wall stock varies, it is very difficult to maintain consistent gloss on the part. Depending on the flow pattern, thinner wall sections may not be exposed to as much plastic pressure, and the result is excess gloss in that area. The same effect can happen when the wall stock becomes too thick; you can get glossy spots because of shrinkage and not being able to pack it out. Gate location can have an impact in adjusting for wall thickness, but whenever you have varying wall stock you are at risk for inconsistent gloss. Insufficient draft angel will creat problems to smooth demolding.Excessive force may be appliedandcause the dull issue.

3.Lack of venting

Lack of venting can cause dull and/or shiny spots or streaks. Venting is often overlooked; if too much gas is entrapped within the cavity due to poor venting, glossy streaks or dots may show up on the part.

 

  1. Inproper design of runner or gate

Runner and or gate size is also considered as a possible solution to gloss problem. If the cross-sectional area of the gate or runner is too small or changes abruptly,the shear force becomes too strong when the melt flows through in a state of turbulent dynamic , resulting in poor gloss. Therefore, the cross-sectional area of the gate and runner should be appropriately increased.

 

ABS Injection molding process

1.Slow injection speed

If the injection speed is too small, the surface of the plastic part is not dense and the gloss is poor. For this reason, the injection speed can be appropriately increased

 

2.Lack of cooling

 

Lack of cooling can also contribute to gloss issues when cavity details or mold components become hotter than the rest of the cavity. Typically in these cases the gloss or read-through will show up shinier.

3.Lower pack/hold pressure

 

Low pack or hold pressure will tend to make your part look glossier
4. Cooler Melt

When the melt flow is too low, the fluidity is poor, which can easily lead to poor gloss, so the melt temperature should be raised appropriately.

Plastic Material

Keep in mind that each material will provide a different level of gloss. It is very important to understand type of material in production. Make sure the the recycled material could not be too much. Materials that contain abrasive additives such as glass fibers can cause gloss issues over time with erosion of the cavity surface. On textured cavities, this will result in a glossier finish as the texture detail is eroded over time.